新款塑料低温脆化试验机检查电线电缆塑料外壳以及硫化橡胶在低温测试时的脆化特性。  

The embrittlement of  plastic case of the wire and the embrittlement of vulcanized rubber during low  temperature test.

用户可以选择TS-BC直线性冲击试验方法或者TS-BT摆锤型冲击试验方法以满足客户对设备的不同需求。  

The user can choose the  TS-BC linear impact test method or TS-BT pendulum type impact test method to  meet the customer's different needs of the equipment.

试验时将试样固定于夹具上，然后将试样浸泡坐在低温介质中5分钟，用2±0.2m/s的线速度冲击试样，后检查试样在温度是否出现裂纹、裂缝、小孔、以及是否完分离成碎片。  

Test sample is fixed on  the fixture, then soaked samples sitting in low temperature medium in 5 minutes,  with 2 + 0.2 M / s line speed impact test specimens, the final inspection sample  in the lowest temperature whether cracks, cracks, holes, and whether separates  into pieces.

通过转换卡盘托架底座可以连续的进行样品测试，可以节省样品放回原处时间，满足很多样品各自的测试标准。  

Through the conversion of  the chuck bracket base can be continuous sample test, can save the sample back  in place of time, meet a lot of samples of the respective test standard.  

新款塑料低温脆化试验机制冷方式 The  refrigeration mode of multifunctional plastic cryogenic embrittlement test  machine
采用二段式压缩机快速降温制冷，温度可达-76℃(如需低于-76℃，可定制)。  

Two stage compressor  cooling refrigeration, the lowest temperature of up to -76 (for example, can be  customized for less than -76).

温度可控性高，低温槽中液体传热介质可启用搅拌马达，使温度均匀性更佳。毎次可测试4组试样， 旋转定位夹具对每组试样进行冲击测试，检査出现脆性破坏的温度。  

The temperature can be  controlled and the heat transfer medium of the liquid in the cryogenic tank can  be used for stirring the motor, and the temperature uniformity is better.. Each  time 4 groups of samples testing, rotary positioning fixture for each specimen  of impact test and laboratory examination appear brittle failure of minimum  temperature.

新款塑料低温脆化试验机测试标准：  

Standard for testing of  multi - functional plastic cryogenic Embrittlement Testing Machine:

GB/T5470-2008塑料冲击法脆化温度的测定  

Determination of  embrittlement temperature of plastic impact method

GB/T  12584-2008橡胶或塑料涂覆织物低温冲击试验  

Low temperature impact  test for rubber or plastic coated fabrics

GB/T15256-1994硫化橡胶低温脆性的测定（多试样法）  

Determination of low  temperature brittleness of vulcanized rubber (Multi - specimen method)4  

ISO 812-2011硫化橡胶或热塑性橡胶--低温脆性的测定  

Vulcanized or  thermoplastic - Determination of low temperature brittleness

BS 903 A25:1992  橡胶的物理试验.第A25部分:低温脆性测定  

Physical tests for rubber  - Determination of low temperature brittleness for part A25

ISO 974-2000塑料.冲击脆化温度的测定  

Plastics. Determination of  impact embrittlement temperature

ASTM  D2137-2010挠性聚合物及其涂覆织物脆化点测试方法  

Test method for brittle  point of flexible polymer and its coated fabric

ASTM D746-2013用冲击法测定塑料及弹性材料脆化温度的试验方法  

Test method for brittle  temperature of plastic and elastomeric materials by impact method

JIS K7216塑料低温脆化测试方法  

Test method for low  temperature embrittlement of plastics

JIS K6261-2006硫化或热塑性橡胶--低温特性的测定  

Vulcanized or  thermoplastic - Determination of low temperature properties

JIS C3005-2000橡胶或塑料绝缘电线和电缆的试验方法  

Test method for rubber or  plastics insulated wires and cable

JIS K  6723-1995增塑聚氯乙烯化合物 Polyvinyl  chloride compound

本标准规定了测定橡胶材料在规定条件下经受冲击时不出现脆性破坏的温度或部分试样出现脆性破坏温度的方法。 
　　本标准适用于硫化橡胶或热塑性橡胶低温脆性的测定。 
　　因为材料的脆性温度受测试条件和冲击速度的影响，这样测得的脆性温度不一定是这种材料可以使用的温度。这种方法获得的数据只有在变形条件和试验规定的条件相似的情况下，才可用于预见橡胶材料在低温下的特性。 
　　描述了三种程序：程序A：测定脆性温度；程序B：测定50%破坏的脆性温度；程序C：在规定温度下冲击试样。 
　　程序C用于橡胶材料的分类及评价橡胶材料符合性。（对于橡胶涂层织物的类似测试见ISO 4646，橡胶或塑料涂层织物低温冲击试验）

脆性温度：

在规定条件下一组试样不产生破坏的温度。

50%脆性温度：

在规定的条件下一组试样50%发生破坏的温度

试验速度：

试样装置的冲击头与被夹紧试样之间冲击时的相对线速度（试验装置可用于满足本标准要求的旋转电机、电磁线圈、重锤、弹簧驱动的冲击器。标准上只给出电磁线圈低温冲击试验机的速度校准，而我公司是采用伺服电机控制冲击速度，所以只需校准伺服电机的转速即可）

●新款塑料低温脆化试验机技术参数：Low  temperature embrittlement testing machine technical parameters - multi  functional plastics